EN 1.0234 Steel vs. C14181 Copper
EN 1.0234 steel belongs to the iron alloys classification, while C14181 copper belongs to the copper alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.0234 steel and the bottom bar is C14181 copper.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 12 to 29 | |
| 15 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 43 |
| Tensile Strength: Ultimate (UTS), MPa | 350 to 480 | |
| 210 |
| Tensile Strength: Yield (Proof), MPa | 220 to 410 | |
| 130 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1080 |
| Melting Onset (Solidus), °C | 1420 | |
| 1080 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 53 | |
| 380 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 31 |
| Density, g/cm3 | 7.9 | |
| 9.0 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.6 |
| Embodied Energy, MJ/kg | 18 | |
| 41 |
| Embodied Water, L/kg | 46 | |
| 310 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 36 to 130 | |
| 28 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 130 to 440 | |
| 69 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.2 |
| Stiffness to Weight: Bending, points | 24 | |
| 18 |
| Strength to Weight: Axial, points | 12 to 17 | |
| 6.5 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 8.8 |
| Thermal Diffusivity, mm2/s | 14 | |
| 110 |
| Thermal Shock Resistance, points | 11 to 15 | |
| 7.4 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Carbon (C), % | 0.13 to 0.17 | |
| 0 to 0.0050 |
| Copper (Cu), % | 0 | |
| 99.9 to 100 |
| Iron (Fe), % | 99.02 to 99.5 | |
| 0 |
| Lead (Pb), % | 0 | |
| 0 to 0.0020 |
| Manganese (Mn), % | 0.35 to 0.6 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.0020 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0020 |