EN 1.0254 Steel vs. S44700 Stainless Steel
Both EN 1.0254 steel and S44700 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.0254 steel and the bottom bar is S44700 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 120 | |
| 200 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Elongation at Break, % | 27 | |
| 23 |
| Fatigue Strength, MPa | 190 | |
| 300 |
| Poisson's Ratio | 0.29 | |
| 0.27 |
| Shear Modulus, GPa | 73 | |
| 82 |
| Shear Strength, MPa | 280 | |
| 380 |
| Tensile Strength: Ultimate (UTS), MPa | 430 | |
| 600 |
| Tensile Strength: Yield (Proof), MPa | 250 | |
| 450 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 300 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 18 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 3.6 |
| Embodied Energy, MJ/kg | 19 | |
| 49 |
| Embodied Water, L/kg | 47 | |
| 180 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 170 | |
| 480 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 15 | |
| 21 |
| Strength to Weight: Bending, points | 16 | |
| 20 |
| Thermal Shock Resistance, points | 14 | |
| 19 |
Alloy Composition
| Carbon (C), % | 0 to 0.16 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0 to 0.3 | |
| 28 to 30 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.15 |
| Iron (Fe), % | 97.2 to 100 | |
| 64.9 to 68.5 |
| Manganese (Mn), % | 0 to 1.2 | |
| 0 to 0.3 |
| Molybdenum (Mo), % | 0 to 0.080 | |
| 3.5 to 4.2 |
| Nickel (Ni), % | 0 to 0.3 | |
| 0 to 0.15 |
| Niobium (Nb), % | 0 to 0.010 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.020 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.35 | |
| 0 to 0.2 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.020 |
| Titanium (Ti), % | 0 to 0.040 | |
| 0 |
| Vanadium (V), % | 0 to 0.020 | |
| 0 |