EN 1.0258 Steel vs. AISI 347 Stainless Steel
Both EN 1.0258 steel and AISI 347 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.0258 steel and the bottom bar is AISI 347 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 | |
| 160 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 23 | |
| 34 to 46 |
| Fatigue Strength, MPa | 200 | |
| 220 to 270 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 310 | |
| 430 to 460 |
| Tensile Strength: Ultimate (UTS), MPa | 490 | |
| 610 to 690 |
| Tensile Strength: Yield (Proof), MPa | 290 | |
| 240 to 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 870 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 49 | |
| 16 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 2.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 2.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 19 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 3.6 |
| Embodied Energy, MJ/kg | 19 | |
| 52 |
| Embodied Water, L/kg | 47 | |
| 150 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 95 | |
| 190 to 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 220 | |
| 150 to 310 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 17 | |
| 22 to 25 |
| Strength to Weight: Bending, points | 18 | |
| 20 to 22 |
| Thermal Diffusivity, mm2/s | 13 | |
| 4.3 |
| Thermal Shock Resistance, points | 16 | |
| 13 to 15 |
Alloy Composition
| Carbon (C), % | 0 to 0.2 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 to 0.3 | |
| 17 to 19 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 96.9 to 100 | |
| 64.1 to 74 |
| Manganese (Mn), % | 0 to 1.4 | |
| 0 to 2.0 |
| Molybdenum (Mo), % | 0 to 0.080 | |
| 0 |
| Nickel (Ni), % | 0 to 0.3 | |
| 9.0 to 13 |
| Niobium (Nb), % | 0 to 0.010 | |
| 0 to 1.0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.030 |
| Titanium (Ti), % | 0 to 0.040 | |
| 0 |
| Vanadium (V), % | 0 to 0.020 | |
| 0 |