EN 1.0303 Steel vs. EN 1.5520 Steel
Both EN 1.0303 steel and EN 1.5520 steel are iron alloys. They have a very high 99% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.0303 steel and the bottom bar is EN 1.5520 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 84 to 120 | |
| 120 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 12 to 25 | |
| 11 to 21 |
| Fatigue Strength, MPa | 150 to 230 | |
| 210 to 300 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 75 to 86 | |
| 62 to 75 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 220 to 260 | |
| 290 to 340 |
| Tensile Strength: Ultimate (UTS), MPa | 290 to 410 | |
| 410 to 1410 |
| Tensile Strength: Yield (Proof), MPa | 200 to 320 | |
| 300 to 480 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1460 |
| Melting Onset (Solidus), °C | 1430 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 53 | |
| 50 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 6.9 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 7.9 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.9 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 19 |
| Embodied Water, L/kg | 46 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 30 to 94 | |
| 42 to 230 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 to 270 | |
| 240 to 600 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 10 to 15 | |
| 15 to 50 |
| Strength to Weight: Bending, points | 12 to 16 | |
| 16 to 36 |
| Thermal Diffusivity, mm2/s | 14 | |
| 13 |
| Thermal Shock Resistance, points | 9.2 to 13 | |
| 12 to 41 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 |
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.020 to 0.060 | |
| 0.15 to 0.2 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 | |
| 0 to 0.25 |
| Iron (Fe), % | 99.335 to 99.71 | |
| 97.7 to 98.9 |
| Manganese (Mn), % | 0.25 to 0.4 | |
| 0.9 to 1.2 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.025 |