EN 1.0411 Steel vs. SAE-AISI 1117 Steel
Both EN 1.0411 steel and SAE-AISI 1117 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.0411 steel and the bottom bar is SAE-AISI 1117 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 120 to 170 | |
| 140 to 150 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 12 to 26 | |
| 17 to 26 |
| Fatigue Strength, MPa | 200 to 320 | |
| 190 to 300 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Reduction in Area, % | 60 to 74 | |
| 46 to 53 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 300 to 350 | |
| 320 to 330 |
| Tensile Strength: Ultimate (UTS), MPa | 420 to 570 | |
| 490 to 540 |
| Tensile Strength: Yield (Proof), MPa | 270 to 480 | |
| 260 to 460 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 52 | |
| 52 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.8 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 18 | |
| 18 |
| Embodied Water, L/kg | 47 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 140 | |
| 86 to 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 610 | |
| 180 to 550 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 17 to 19 |
| Strength to Weight: Bending, points | 16 to 20 | |
| 18 to 19 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 13 to 18 | |
| 15 to 17 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 |
| Carbon (C), % | 0.18 to 0.22 | |
| 0.14 to 0.2 |
| Iron (Fe), % | 98.7 to 99.1 | |
| 98.3 to 98.8 |
| Manganese (Mn), % | 0.7 to 0.9 | |
| 1.0 to 1.3 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.080 to 0.13 |