EN 1.0411 Steel vs. C65500 Bronze
EN 1.0411 steel belongs to the iron alloys classification, while C65500 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.0411 steel and the bottom bar is C65500 bronze.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 12 to 26 | |
| 4.0 to 70 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 43 |
| Shear Strength, MPa | 300 to 350 | |
| 260 to 440 |
| Tensile Strength: Ultimate (UTS), MPa | 420 to 570 | |
| 360 to 760 |
| Tensile Strength: Yield (Proof), MPa | 270 to 480 | |
| 120 to 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 200 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1030 |
| Melting Onset (Solidus), °C | 1420 | |
| 970 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 400 |
| Thermal Conductivity, W/m-K | 52 | |
| 36 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 7.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 7.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 29 |
| Density, g/cm3 | 7.9 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.7 |
| Embodied Energy, MJ/kg | 18 | |
| 42 |
| Embodied Water, L/kg | 47 | |
| 300 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 140 | |
| 11 to 450 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 610 | |
| 62 to 790 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.5 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 12 to 24 |
| Strength to Weight: Bending, points | 16 to 20 | |
| 13 to 21 |
| Thermal Diffusivity, mm2/s | 14 | |
| 10 |
| Thermal Shock Resistance, points | 13 to 18 | |
| 12 to 26 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0 |
| Carbon (C), % | 0.18 to 0.22 | |
| 0 |
| Copper (Cu), % | 0 | |
| 91.5 to 96.7 |
| Iron (Fe), % | 98.7 to 99.1 | |
| 0 to 0.8 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 0.7 to 0.9 | |
| 0.5 to 1.3 |
| Nickel (Ni), % | 0 | |
| 0 to 0.6 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.1 | |
| 2.8 to 3.8 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.5 |
| Residuals, % | 0 | |
| 0 to 0.5 |