EN 1.0411 Steel vs. N10629 Nickel
EN 1.0411 steel belongs to the iron alloys classification, while N10629 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.0411 steel and the bottom bar is N10629 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 12 to 26 | |
| 45 |
| Fatigue Strength, MPa | 200 to 320 | |
| 340 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 73 | |
| 83 |
| Shear Strength, MPa | 300 to 350 | |
| 600 |
| Tensile Strength: Ultimate (UTS), MPa | 420 to 570 | |
| 860 |
| Tensile Strength: Yield (Proof), MPa | 270 to 480 | |
| 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 910 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1610 |
| Melting Onset (Solidus), °C | 1420 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Expansion, µm/m-K | 12 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 75 |
| Density, g/cm3 | 7.9 | |
| 9.2 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 15 |
| Embodied Energy, MJ/kg | 18 | |
| 190 |
| Embodied Water, L/kg | 47 | |
| 270 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 43 to 140 | |
| 320 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 to 610 | |
| 360 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 22 |
| Strength to Weight: Axial, points | 15 to 20 | |
| 26 |
| Strength to Weight: Bending, points | 16 to 20 | |
| 22 |
| Thermal Shock Resistance, points | 13 to 18 | |
| 27 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.060 | |
| 0.1 to 0.5 |
| Carbon (C), % | 0.18 to 0.22 | |
| 0 to 0.010 |
| Chromium (Cr), % | 0 | |
| 0.5 to 1.5 |
| Cobalt (Co), % | 0 | |
| 0 to 2.5 |
| Copper (Cu), % | 0 | |
| 0 to 0.5 |
| Iron (Fe), % | 98.7 to 99.1 | |
| 1.0 to 6.0 |
| Manganese (Mn), % | 0.7 to 0.9 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 26 to 30 |
| Nickel (Ni), % | 0 | |
| 65 to 72.4 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.010 |