EN 1.0446 Cast Steel vs. C72800 Copper-nickel
EN 1.0446 cast steel belongs to the iron alloys classification, while C72800 copper-nickel belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.0446 cast steel and the bottom bar is C72800 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 120 |
| Elongation at Break, % | 25 | |
| 3.9 to 23 |
| Poisson's Ratio | 0.29 | |
| 0.34 |
| Shear Modulus, GPa | 73 | |
| 44 |
| Tensile Strength: Ultimate (UTS), MPa | 530 | |
| 520 to 1270 |
| Tensile Strength: Yield (Proof), MPa | 270 | |
| 250 to 1210 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 210 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 200 |
| Melting Completion (Liquidus), °C | 1470 | |
| 1080 |
| Melting Onset (Solidus), °C | 1430 | |
| 920 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 53 | |
| 55 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.8 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.9 | |
| 11 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.7 | |
| 38 |
| Density, g/cm3 | 7.9 | |
| 8.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 4.4 |
| Embodied Energy, MJ/kg | 18 | |
| 68 |
| Embodied Water, L/kg | 45 | |
| 360 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 | |
| 37 to 99 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 190 | |
| 260 to 5650 |
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 19 | |
| 17 to 40 |
| Strength to Weight: Bending, points | 18 | |
| 16 to 30 |
| Thermal Diffusivity, mm2/s | 14 | |
| 17 |
| Thermal Shock Resistance, points | 17 | |
| 19 to 45 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0 to 0.1 |
| Antimony (Sb), % | 0 | |
| 0 to 0.020 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.0010 |
| Boron (B), % | 0 | |
| 0 to 0.0010 |
| Copper (Cu), % | 0 | |
| 78.3 to 82.8 |
| Iron (Fe), % | 99.935 to 100 | |
| 0 to 0.5 |
| Lead (Pb), % | 0 | |
| 0 to 0.0050 |
| Magnesium (Mg), % | 0 | |
| 0.0050 to 0.15 |
| Manganese (Mn), % | 0 | |
| 0.050 to 0.3 |
| Nickel (Ni), % | 0 | |
| 9.5 to 10.5 |
| Niobium (Nb), % | 0 | |
| 0.1 to 0.3 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.0050 |
| Silicon (Si), % | 0 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.0025 |
| Tin (Sn), % | 0 | |
| 7.5 to 8.5 |
| Titanium (Ti), % | 0 | |
| 0 to 0.010 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.3 |