EN 1.0455 (GS240) Cast Non-Alloy Steel
EN 1.0455 cast steel is a carbon steel formulated for casting. Cited properties are appropriate for the normalized condition. 1.0455 is the EN numeric designation for this material. GS240 is the EN chemical designation.
The graph bars on the material properties cards below compare EN 1.0455 cast steel to: cast carbon steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.
Mechanical Properties
Elastic (Young's, Tensile) Modulus
190 GPa 27 x 106 psi
Elongation at Break
25 %
Fatigue Strength
200 MPa 28 x 103 psi
Impact Strength: V-Notched Charpy
35 J 26 ft-lb
Poisson's Ratio
0.29
Shear Modulus
73 GPa 11 x 106 psi
Tensile Strength: Ultimate (UTS)
530 MPa 76 x 103 psi
Tensile Strength: Yield (Proof)
270 MPa 39 x 103 psi
Thermal Properties
Latent Heat of Fusion
250 J/g
Maximum Temperature: Mechanical
400 °C 750 °F
Melting Completion (Liquidus)
1460 °C 2660 °F
Melting Onset (Solidus)
1420 °C 2590 °F
Specific Heat Capacity
470 J/kg-K 0.11 BTU/lb-°F
Thermal Conductivity
52 W/m-K 30 BTU/h-ft-°F
Thermal Expansion
12 µm/m-K
Electrical Properties
Electrical Conductivity: Equal Volume
7.1 % IACS
Electrical Conductivity: Equal Weight (Specific)
8.1 % IACS
Otherwise Unclassified Properties
Base Metal Price
1.8 % relative
Density
7.8 g/cm3 490 lb/ft3
Embodied Carbon
1.4 kg CO2/kg material
Embodied Energy
18 MJ/kg 7.9 x 103 BTU/lb
Embodied Water
46 L/kg 5.4 gal/lb
Common Calculations
Resilience: Ultimate (Unit Rupture Work)
110 MJ/m3
Resilience: Unit (Modulus of Resilience)
190 kJ/m3
Stiffness to Weight: Axial
13 points
Stiffness to Weight: Bending
24 points
Strength to Weight: Axial
19 points
Strength to Weight: Bending
18 points
Thermal Diffusivity
14 mm2/s
Thermal Shock Resistance
17 points
Alloy Composition
| Fe | 97.9 to 100 | |
| Mn | 0 to 1.2 | |
| Si | 0 to 0.6 | |
| C | 0 to 0.23 | |
| P | 0 to 0.030 | |
| S | 0 to 0.025 |
All values are % weight. Ranges represent what is permitted under applicable standards.
Followup Questions
Similar Alloys
Further Reading
EN 10293: Steel castings - Steel castings for general engineering uses
Properties and Selection: Irons, Steels and High Performance Alloys, ASM Handbook vol. 1, ASM International, 1993
Carbon Steel Handbook, D. Gandy, 2007
Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008
CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015
Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015