EN 1.0540 Steel vs. N07776 Nickel

EN 1.0540 steel belongs to the iron alloys classification, while N07776 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0540 steel and the bottom bar is N07776 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14
39
Fatigue Strength, MPa 210
220
Poisson's Ratio 0.29
0.3
Shear Modulus, GPa 72
79
Shear Strength, MPa 400
470
Tensile Strength: Ultimate (UTS), MPa 660
700
Tensile Strength: Yield (Proof), MPa 330
270

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
970
Melting Completion (Liquidus), °C 1460
1550
Melting Onset (Solidus), °C 1420
1500
Specific Heat Capacity, J/kg-K 470
430
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
85
Density, g/cm3 7.8
8.6
Embodied Carbon, kg CO2/kg material 1.4
15
Embodied Energy, MJ/kg 19
210
Embodied Water, L/kg 47
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 75
220
Resilience: Unit (Modulus of Resilience), kJ/m3 290
180
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 23
22
Strength to Weight: Bending, points 22
20
Thermal Shock Resistance, points 21
20

Alloy Composition

Aluminum (Al), % 0
0 to 2.0
Carbon (C), % 0.47 to 0.55
0 to 0.030
Chromium (Cr), % 0 to 0.4
12 to 22
Iron (Fe), % 97.2 to 98.9
0 to 24.5
Manganese (Mn), % 0.6 to 0.9
0 to 1.0
Molybdenum (Mo), % 0 to 0.1
9.0 to 15
Nickel (Ni), % 0 to 0.4
50 to 60
Niobium (Nb), % 0
4.0 to 6.0
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.045
0 to 0.010
Titanium (Ti), % 0
0 to 1.0
Tungsten (W), % 0
0.5 to 2.5