EN 1.0558 Cast Steel vs. 3105 Aluminum

EN 1.0558 cast steel belongs to the iron alloys classification, while 3105 aluminum belongs to the aluminum alloys. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.0558 cast steel and the bottom bar is 3105 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
69
Elongation at Break, % 18
1.1 to 20
Fatigue Strength, MPa 230
39 to 95
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 73
26
Tensile Strength: Ultimate (UTS), MPa 640
120 to 240
Tensile Strength: Yield (Proof), MPa 340
46 to 220

Thermal Properties

Latent Heat of Fusion, J/g 250
400
Maximum Temperature: Mechanical, °C 400
180
Melting Completion (Liquidus), °C 1470
660
Melting Onset (Solidus), °C 1430
640
Specific Heat Capacity, J/kg-K 470
900
Thermal Conductivity, W/m-K 53
170
Thermal Expansion, µm/m-K 12
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.8
44
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
140

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
9.5
Density, g/cm3 7.9
2.8
Embodied Carbon, kg CO2/kg material 1.4
8.2
Embodied Energy, MJ/kg 18
150
Embodied Water, L/kg 45
1180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 99
2.6 to 19
Resilience: Unit (Modulus of Resilience), kJ/m3 300
15 to 340
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
50
Strength to Weight: Axial, points 22
12 to 24
Strength to Weight: Bending, points 21
20 to 31
Thermal Diffusivity, mm2/s 14
68
Thermal Shock Resistance, points 20
5.2 to 11

Alloy Composition

Aluminum (Al), % 0
96 to 99.5
Chromium (Cr), % 0
0 to 0.2
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 99.935 to 100
0 to 0.7
Magnesium (Mg), % 0
0.2 to 0.8
Manganese (Mn), % 0
0.3 to 0.8
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0
0 to 0.6
Sulfur (S), % 0 to 0.030
0
Titanium (Ti), % 0
0 to 0.1
Zinc (Zn), % 0
0 to 0.4
Residuals, % 0
0 to 0.15