EN 1.0571 Steel vs. SAE-AISI 5120 Steel

Both EN 1.0571 steel and SAE-AISI 5120 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0571 steel and the bottom bar is SAE-AISI 5120 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
16
Fatigue Strength, MPa 220
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 350
310
Tensile Strength: Ultimate (UTS), MPa 550
500
Tensile Strength: Yield (Proof), MPa 310
320

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 52
47
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.3
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.6
1.4
Embodied Energy, MJ/kg 21
19
Embodied Water, L/kg 49
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
71
Resilience: Unit (Modulus of Resilience), kJ/m3 260
280
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
18
Strength to Weight: Bending, points 19
18
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 17
16

Alloy Composition

Aluminum (Al), % 0 to 0.060
0
Carbon (C), % 0 to 0.2
0.17 to 0.22
Chromium (Cr), % 0 to 0.3
0.7 to 0.9
Copper (Cu), % 0 to 0.2
0
Iron (Fe), % 96.5 to 99
97.6 to 98.3
Manganese (Mn), % 0.9 to 1.7
0.7 to 0.9
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.050
0
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.1 to 0.5
0.15 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.040
Vanadium (V), % 0 to 0.1
0