EN 1.0591 Cast Steel vs. AWS ENiCrFe-2

EN 1.0591 cast steel belongs to the iron alloys classification, while AWS ENiCrFe-2 belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.0591 cast steel and the bottom bar is AWS ENiCrFe-2.

EN 1.0591 (GE320) Cast Non-Alloy Steel AWS ENiCrFe-2 (W86133) Weld Metal

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa		190
Elastic (Young's, Tensile) Modulus, GPa		190

Elongation at Break, %		19
Elongation at Break, %		28

Poisson's Ratio		0.29
Poisson's Ratio		0.3

Shear Modulus, GPa		73
Shear Modulus, GPa		74

Tensile Strength: Ultimate (UTS), MPa		620
Tensile Strength: Ultimate (UTS), MPa		790

Thermal Properties

Latent Heat of Fusion, J/g		250
Latent Heat of Fusion, J/g		310

Melting Completion (Liquidus), °C		1470
Melting Completion (Liquidus), °C		1390

Melting Onset (Solidus), °C		1430
Melting Onset (Solidus), °C		1350

Specific Heat Capacity, J/kg-K		470
Specific Heat Capacity, J/kg-K		450

Thermal Expansion, µm/m-K		12
Thermal Expansion, µm/m-K		12

Otherwise Unclassified Properties

Base Metal Price, % relative		1.7
Base Metal Price, % relative		65

Density, g/cm³		7.9
Density, g/cm³		8.5

Embodied Carbon, kg CO₂/kg material		1.4
Embodied Carbon, kg CO₂/kg material		11

Embodied Energy, MJ/kg		18
Embodied Energy, MJ/kg		160

Embodied Water, L/kg		45
Embodied Water, L/kg		260

Common Calculations

Stiffness to Weight: Axial, points		13
Stiffness to Weight: Axial, points		13

Stiffness to Weight: Bending, points		24
Stiffness to Weight: Bending, points		23

Strength to Weight: Axial, points		22
Strength to Weight: Axial, points		26

Strength to Weight: Bending, points		20
Strength to Weight: Bending, points		22

Thermal Shock Resistance, points		20
Thermal Shock Resistance, points		24

Alloy Composition

Carbon (C), %		0
Carbon (C), %		0 to 0.1

Chromium (Cr), %		0
Chromium (Cr), %		13 to 17

Cobalt (Co), %		0
Cobalt (Co), %		0 to 0.12

Copper (Cu), %		0
Copper (Cu), %		0 to 0.5

Iron (Fe), %		99.935 to 100
Iron (Fe), %		0 to 12

Manganese (Mn), %		0
Manganese (Mn), %		1.0 to 3.5

Molybdenum (Mo), %		0
Molybdenum (Mo), %		0.5 to 2.5

Nickel (Ni), %		0
Nickel (Ni), %		62 to 85

Niobium (Nb), %		0
Niobium (Nb), %		0.5 to 4.0

Phosphorus (P), %		0 to 0.035
Phosphorus (P), %		0 to 0.030

Silicon (Si), %		0
Silicon (Si), %		0 to 0.75

Sulfur (S), %		0 to 0.030
Sulfur (S), %		0 to 0.020

Residuals, %		0
Residuals, %		0 to 0.5