EN 1.0597 Cast Steel vs. EN 1.4805 Stainless Steel

Both EN 1.0597 cast steel and EN 1.4805 stainless steel are iron alloys. They have 51% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.0597 cast steel and the bottom bar is EN 1.4805 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 18
9.0
Fatigue Strength, MPa 270
130
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Tensile Strength: Ultimate (UTS), MPa 670
490
Tensile Strength: Yield (Proof), MPa 400
250

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1470
1390
Melting Onset (Solidus), °C 1430
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
14
Thermal Expansion, µm/m-K 12
16

Otherwise Unclassified Properties

Base Metal Price, % relative 1.7
26
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
4.7
Embodied Energy, MJ/kg 18
66
Embodied Water, L/kg 45
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
37
Resilience: Unit (Modulus of Resilience), kJ/m3 430
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 24
17
Strength to Weight: Bending, points 22
18
Thermal Diffusivity, mm2/s 14
3.7
Thermal Shock Resistance, points 21
11

Alloy Composition

Carbon (C), % 0
0.2 to 0.5
Chromium (Cr), % 0
19 to 23
Iron (Fe), % 99.935 to 100
44.9 to 56.8
Manganese (Mn), % 0
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.5
Nickel (Ni), % 0
23 to 27
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0
1.0 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.030