EN 1.1061 Steel vs. EN 1.4570 Stainless Steel

Both EN 1.1061 steel and EN 1.4570 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.1061 steel and the bottom bar is EN 1.4570 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
77
Tensile Strength: Ultimate (UTS), MPa 530 to 1810
610

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
930
Melting Completion (Liquidus), °C 1460
1420
Melting Onset (Solidus), °C 1420
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
2.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
2.8

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
15
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.1
Embodied Energy, MJ/kg 19
43
Embodied Water, L/kg 46
150

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 19 to 64
22
Strength to Weight: Bending, points 19 to 42
20
Thermal Diffusivity, mm2/s 14
4.0
Thermal Shock Resistance, points 17 to 58
14

Alloy Composition

Carbon (C), % 0.42 to 0.5
0 to 0.080
Chromium (Cr), % 0
17 to 19
Copper (Cu), % 0 to 0.25
1.4 to 1.8
Iron (Fe), % 98.1 to 99.06
65 to 73.5
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0
0 to 0.6
Nickel (Ni), % 0
8.0 to 10
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.3
0 to 1.0
Sulfur (S), % 0.020 to 0.035
0.15 to 0.35