EN 1.1061 Steel vs. EN AC-46100 Aluminum

EN 1.1061 steel belongs to the iron alloys classification, while EN AC-46100 aluminum belongs to the aluminum alloys. There are 25 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.1061 steel and the bottom bar is EN AC-46100 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150 to 180
91
Elastic (Young's, Tensile) Modulus, GPa 190
73
Poisson's Ratio 0.29
0.33
Shear Modulus, GPa 72
28
Tensile Strength: Ultimate (UTS), MPa 530 to 1810
270

Thermal Properties

Latent Heat of Fusion, J/g 250
550
Maximum Temperature: Mechanical, °C 400
180
Melting Completion (Liquidus), °C 1460
600
Melting Onset (Solidus), °C 1420
540
Specific Heat Capacity, J/kg-K 470
890
Thermal Conductivity, W/m-K 51
110
Thermal Expansion, µm/m-K 12
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
28
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
90

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
10
Density, g/cm3 7.8
2.7
Embodied Carbon, kg CO2/kg material 1.4
7.6
Embodied Energy, MJ/kg 19
140
Embodied Water, L/kg 46
1030

Common Calculations

Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
51
Strength to Weight: Axial, points 19 to 64
27
Strength to Weight: Bending, points 19 to 42
34
Thermal Diffusivity, mm2/s 14
44
Thermal Shock Resistance, points 17 to 58
12

Alloy Composition

Aluminum (Al), % 0
80.4 to 88.5
Carbon (C), % 0.42 to 0.5
0
Chromium (Cr), % 0
0 to 0.15
Copper (Cu), % 0 to 0.25
1.5 to 2.5
Iron (Fe), % 98.1 to 99.06
0 to 1.1
Lead (Pb), % 0
0 to 0.25
Magnesium (Mg), % 0
0 to 0.3
Manganese (Mn), % 0.5 to 0.8
0 to 0.55
Nickel (Ni), % 0
0 to 0.45
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.3
10 to 12
Sulfur (S), % 0.020 to 0.035
0
Tin (Sn), % 0
0 to 0.15
Titanium (Ti), % 0
0 to 0.25
Zinc (Zn), % 0
0 to 1.7
Residuals, % 0
0 to 0.25