EN 1.1106 Steel vs. EN 1.5522 Steel
Both EN 1.1106 steel and EN 1.5522 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.1106 steel and the bottom bar is EN 1.5522 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 160 | |
| 140 to 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 24 | |
| 11 to 21 |
| Fatigue Strength, MPa | 270 | |
| 210 to 330 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 350 | |
| 320 to 380 |
| Tensile Strength: Ultimate (UTS), MPa | 550 | |
| 450 to 1490 |
| Tensile Strength: Yield (Proof), MPa | 370 | |
| 300 to 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.3 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 22 | |
| 19 |
| Embodied Water, L/kg | 50 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 | |
| 45 to 250 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 360 | |
| 250 to 720 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 19 | |
| 16 to 53 |
| Strength to Weight: Bending, points | 19 | |
| 17 to 37 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 17 | |
| 13 to 44 |
Alloy Composition
| Aluminum (Al), % | 0.020 to 0.024 | |
| 0 |
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.18 | |
| 0.2 to 0.24 |
| Chromium (Cr), % | 0 to 0.3 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.25 |
| Iron (Fe), % | 96.2 to 98.9 | |
| 98 to 98.9 |
| Manganese (Mn), % | 1.1 to 1.7 | |
| 0.9 to 1.2 |
| Molybdenum (Mo), % | 0 to 0.080 | |
| 0 |
| Nickel (Ni), % | 0 to 0.5 | |
| 0 |
| Niobium (Nb), % | 0 to 0.050 | |
| 0 |
| Nitrogen (N), % | 0 to 0.012 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.025 |
| Titanium (Ti), % | 0 to 0.030 | |
| 0 |
| Vanadium (V), % | 0 to 0.1 | |
| 0 |