MakeItFrom.com
Menu (ESC)

EN 1.1118 Cast Steel vs. ASTM A182 Grade F11 Class 1

Both EN 1.1118 cast steel and ASTM A182 grade F11 class 1 are iron alloys. They have a very high 98% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.1118 cast steel and the bottom bar is ASTM A182 grade F11 class 1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14 to 21
23
Fatigue Strength, MPa 320 to 400
160
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 700 to 750
470
Tensile Strength: Yield (Proof), MPa 460 to 630
230

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
430
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.6
Embodied Energy, MJ/kg 19
21
Embodied Water, L/kg 48
52

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 97 to 130
89
Resilience: Unit (Modulus of Resilience), kJ/m3 550 to 1050
140
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
17
Strength to Weight: Bending, points 22 to 23
17
Thermal Diffusivity, mm2/s 14
11
Thermal Shock Resistance, points 22 to 24
14

Alloy Composition

Carbon (C), % 0.2 to 0.25
0.050 to 0.15
Chromium (Cr), % 0
1.0 to 1.5
Iron (Fe), % 97.3 to 98.3
96 to 97.7
Manganese (Mn), % 1.5 to 1.8
0.3 to 0.6
Molybdenum (Mo), % 0
0.44 to 0.65
Phosphorus (P), % 0 to 0.020
0 to 0.030
Silicon (Si), % 0 to 0.6
0.5 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030