EN 1.1118 Cast Steel vs. Nickel 684

EN 1.1118 cast steel belongs to the iron alloys classification, while nickel 684 belongs to the nickel alloys. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.1118 cast steel and the bottom bar is nickel 684.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 14 to 21
11
Fatigue Strength, MPa 320 to 400
390
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
76
Tensile Strength: Ultimate (UTS), MPa 700 to 750
1190
Tensile Strength: Yield (Proof), MPa 460 to 630
800

Thermal Properties

Latent Heat of Fusion, J/g 250
320
Maximum Temperature: Mechanical, °C 400
1000
Melting Completion (Liquidus), °C 1460
1370
Melting Onset (Solidus), °C 1420
1320
Specific Heat Capacity, J/kg-K 470
470
Thermal Expansion, µm/m-K 12
13

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
75
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 1.4
10
Embodied Energy, MJ/kg 19
140
Embodied Water, L/kg 48
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 97 to 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 550 to 1050
1610
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 25 to 27
40
Strength to Weight: Bending, points 22 to 23
30
Thermal Shock Resistance, points 22 to 24
34

Alloy Composition

Aluminum (Al), % 0
2.5 to 3.3
Boron (B), % 0
0.0030 to 0.010
Carbon (C), % 0.2 to 0.25
0 to 0.15
Chromium (Cr), % 0
15 to 20
Cobalt (Co), % 0
13 to 20
Copper (Cu), % 0
0 to 0.15
Iron (Fe), % 97.3 to 98.3
0 to 4.0
Manganese (Mn), % 1.5 to 1.8
0 to 0.75
Molybdenum (Mo), % 0
3.0 to 5.0
Nickel (Ni), % 0
42.7 to 64
Phosphorus (P), % 0 to 0.020
0 to 0.015
Silicon (Si), % 0 to 0.6
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0
2.5 to 3.3