EN 1.1118 Cast Steel vs. S44700 Stainless Steel

Both EN 1.1118 cast steel and S44700 stainless steel are iron alloys. They have 67% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.1118 cast steel and the bottom bar is S44700 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
210
Elongation at Break, % 14 to 21
23
Fatigue Strength, MPa 320 to 400
300
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
82
Tensile Strength: Ultimate (UTS), MPa 700 to 750
600
Tensile Strength: Yield (Proof), MPa 460 to 630
450

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 12
11

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
3.6
Embodied Energy, MJ/kg 19
49
Embodied Water, L/kg 48
180

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 97 to 130
120
Resilience: Unit (Modulus of Resilience), kJ/m3 550 to 1050
480
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 25 to 27
21
Strength to Weight: Bending, points 22 to 23
20
Thermal Shock Resistance, points 22 to 24
19

Alloy Composition

Carbon (C), % 0.2 to 0.25
0 to 0.010
Chromium (Cr), % 0
28 to 30
Copper (Cu), % 0
0 to 0.15
Iron (Fe), % 97.3 to 98.3
64.9 to 68.5
Manganese (Mn), % 1.5 to 1.8
0 to 0.3
Molybdenum (Mo), % 0
3.5 to 4.2
Nickel (Ni), % 0
0 to 0.15
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.6
0 to 0.2
Sulfur (S), % 0 to 0.015
0 to 0.020