EN 1.1122 Steel vs. 390.0 Aluminum
EN 1.1122 steel belongs to the iron alloys classification, while 390.0 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is EN 1.1122 steel and the bottom bar is 390.0 aluminum.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 100 to 130 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 75 |
| Elongation at Break, % | 12 to 21 | |
| 1.0 |
| Fatigue Strength, MPa | 170 to 260 | |
| 76 to 110 |
| Poisson's Ratio | 0.29 | |
| 0.33 |
| Shear Modulus, GPa | 73 | |
| 28 |
| Tensile Strength: Ultimate (UTS), MPa | 340 to 460 | |
| 280 to 300 |
| Tensile Strength: Yield (Proof), MPa | 240 to 370 | |
| 240 to 270 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 640 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 170 |
| Melting Completion (Liquidus), °C | 1460 | |
| 650 |
| Melting Onset (Solidus), °C | 1420 | |
| 560 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 880 |
| Thermal Conductivity, W/m-K | 51 | |
| 130 |
| Thermal Expansion, µm/m-K | 12 | |
| 18 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
| 24 to 25 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
| 79 to 83 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 11 |
| Density, g/cm3 | 7.9 | |
| 2.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 7.3 |
| Embodied Energy, MJ/kg | 18 | |
| 130 |
| Embodied Water, L/kg | 46 | |
| 950 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 36 to 89 | |
| 2.7 to 2.9 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 360 | |
| 380 to 470 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 52 |
| Strength to Weight: Axial, points | 12 to 16 | |
| 28 to 30 |
| Strength to Weight: Bending, points | 14 to 17 | |
| 35 to 36 |
| Thermal Diffusivity, mm2/s | 14 | |
| 56 |
| Thermal Shock Resistance, points | 11 to 15 | |
| 14 to 15 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 74.5 to 79.6 |
| Carbon (C), % | 0.080 to 0.12 | |
| 0 |
| Copper (Cu), % | 0 to 0.25 | |
| 4.0 to 5.0 |
| Iron (Fe), % | 98.7 to 99.62 | |
| 0 to 1.3 |
| Magnesium (Mg), % | 0 | |
| 0.45 to 0.65 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 0.1 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.3 | |
| 16 to 18 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 0 to 0.2 |
| Zinc (Zn), % | 0 | |
| 0 to 0.1 |
| Residuals, % | 0 | |
| 0 to 0.2 |