EN 1.1127 Steel vs. ASTM A217 Cast Steel

Both EN 1.1127 steel and ASTM A217 cast steel are iron alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.1127 steel and the bottom bar is ASTM A217 cast steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 230
160 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 14 to 25
21 to 27
Fatigue Strength, MPa 280 to 370
200 to 320
Poisson's Ratio 0.29
0.28 to 0.29
Shear Modulus, GPa 73
73 to 75
Tensile Strength: Ultimate (UTS), MPa 660 to 790
540 to 710
Tensile Strength: Yield (Proof), MPa 410 to 580
270 to 460

Thermal Properties

Latent Heat of Fusion, J/g 250
250 to 270
Maximum Temperature: Mechanical, °C 400
410 to 600
Melting Completion (Liquidus), °C 1460
1450 to 1460
Melting Onset (Solidus), °C 1410
1410 to 1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
26 to 50
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.3 to 9.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.4 to 11

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.4 to 7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.5 to 2.1
Embodied Energy, MJ/kg 19
20 to 28
Embodied Water, L/kg 49
47 to 87

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 90 to 140
110 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 440 to 880
190 to 570
Stiffness to Weight: Axial, points 13
13 to 14
Stiffness to Weight: Bending, points 24
24 to 25
Strength to Weight: Axial, points 23 to 28
19 to 25
Strength to Weight: Bending, points 22 to 24
19 to 23
Thermal Diffusivity, mm2/s 13
6.9 to 14
Thermal Shock Resistance, points 21 to 25
16 to 20