EN 1.1127 Steel vs. EN 1.0220 Steel
Both EN 1.1127 steel and EN 1.0220 steel are iron alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.1127 steel and the bottom bar is EN 1.0220 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 230 | |
| 110 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 to 25 | |
| 23 |
| Fatigue Strength, MPa | 280 to 370 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 420 to 480 | |
| 250 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 790 | |
| 390 |
| Tensile Strength: Yield (Proof), MPa | 410 to 580 | |
| 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 49 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 8.1 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 18 |
| Embodied Water, L/kg | 49 | |
| 46 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 90 to 140 | |
| 80 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 440 to 880 | |
| 230 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 28 | |
| 14 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 15 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 21 to 25 | |
| 12 |
Alloy Composition
| Carbon (C), % | 0.34 to 0.42 | |
| 0 to 0.16 |
| Chromium (Cr), % | 0 to 0.4 | |
| 0 |
| Iron (Fe), % | 96.6 to 98.1 | |
| 98.2 to 100 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0 to 1.2 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.045 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.35 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.045 |