EN 1.1127 Steel vs. EN 1.4923 Stainless Steel
Both EN 1.1127 steel and EN 1.4923 stainless steel are iron alloys. They have 87% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.1127 steel and the bottom bar is EN 1.4923 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 14 to 25 | |
| 12 to 21 |
| Fatigue Strength, MPa | 280 to 370 | |
| 300 to 440 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 76 |
| Shear Strength, MPa | 420 to 480 | |
| 540 to 590 |
| Tensile Strength: Ultimate (UTS), MPa | 660 to 790 | |
| 870 to 980 |
| Tensile Strength: Yield (Proof), MPa | 410 to 580 | |
| 470 to 780 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 740 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1450 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 49 | |
| 24 |
| Thermal Expansion, µm/m-K | 12 | |
| 11 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 2.9 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 3.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 8.0 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 2.9 |
| Embodied Energy, MJ/kg | 19 | |
| 41 |
| Embodied Water, L/kg | 49 | |
| 100 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 90 to 140 | |
| 110 to 150 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 440 to 880 | |
| 570 to 1580 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 23 to 28 | |
| 31 to 35 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 26 to 28 |
| Thermal Diffusivity, mm2/s | 13 | |
| 6.5 |
| Thermal Shock Resistance, points | 21 to 25 | |
| 30 to 34 |
Alloy Composition
| Carbon (C), % | 0.34 to 0.42 | |
| 0.18 to 0.24 |
| Chromium (Cr), % | 0 to 0.4 | |
| 11 to 12.5 |
| Iron (Fe), % | 96.6 to 98.1 | |
| 83.5 to 87.1 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0.4 to 0.9 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0.8 to 1.2 |
| Nickel (Ni), % | 0 to 0.4 | |
| 0.3 to 0.8 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.015 |
| Vanadium (V), % | 0 | |
| 0.25 to 0.35 |