EN 1.1132 Steel vs. CC332G Bronze
EN 1.1132 steel belongs to the iron alloys classification, while CC332G bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is EN 1.1132 steel and the bottom bar is CC332G bronze.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 110 to 140 | |
130 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
120 |
Elongation at Break, % | 12 to 24 | |
22 |
Poisson's Ratio | 0.29 | |
0.34 |
Shear Modulus, GPa | 73 | |
43 |
Tensile Strength: Ultimate (UTS), MPa | 370 to 490 | |
620 |
Tensile Strength: Yield (Proof), MPa | 240 to 400 | |
250 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
230 |
Maximum Temperature: Mechanical, °C | 400 | |
220 |
Melting Completion (Liquidus), °C | 1460 | |
1060 |
Melting Onset (Solidus), °C | 1420 | |
1010 |
Specific Heat Capacity, J/kg-K | 470 | |
440 |
Thermal Conductivity, W/m-K | 51 | |
45 |
Thermal Expansion, µm/m-K | 12 | |
18 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.0 | |
11 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.0 | |
12 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.8 | |
29 |
Density, g/cm3 | 7.9 | |
8.3 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
3.4 |
Embodied Energy, MJ/kg | 18 | |
55 |
Embodied Water, L/kg | 46 | |
390 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 38 to 110 | |
110 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 160 to 430 | |
270 |
Stiffness to Weight: Axial, points | 13 | |
7.7 |
Stiffness to Weight: Bending, points | 24 | |
20 |
Strength to Weight: Axial, points | 13 to 17 | |
21 |
Strength to Weight: Bending, points | 15 to 18 | |
19 |
Thermal Diffusivity, mm2/s | 14 | |
12 |
Thermal Shock Resistance, points | 12 to 16 | |
21 |
Alloy Composition
Aluminum (Al), % | 0 | |
8.5 to 10.5 |
Carbon (C), % | 0.13 to 0.17 | |
0 |
Copper (Cu), % | 0 to 0.25 | |
80 to 86 |
Iron (Fe), % | 98.6 to 99.57 | |
1.0 to 3.0 |
Lead (Pb), % | 0 | |
0 to 0.1 |
Magnesium (Mg), % | 0 | |
0 to 0.050 |
Manganese (Mn), % | 0.3 to 0.6 | |
0 to 2.0 |
Nickel (Ni), % | 0 | |
1.5 to 4.0 |
Phosphorus (P), % | 0 to 0.025 | |
0 |
Silicon (Si), % | 0 to 0.3 | |
0 to 0.2 |
Sulfur (S), % | 0 to 0.025 | |
0 |
Tin (Sn), % | 0 | |
0 to 0.2 |
Zinc (Zn), % | 0 | |
0 to 0.5 |