EN 1.1133 Steel vs. Nickel 684
EN 1.1133 steel belongs to the iron alloys classification, while nickel 684 belongs to the nickel alloys. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.1133 steel and the bottom bar is nickel 684.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 170 to 180 | |
310 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
200 |
Elongation at Break, % | 19 to 24 | |
11 |
Fatigue Strength, MPa | 230 to 310 | |
390 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 73 | |
76 |
Shear Strength, MPa | 370 to 380 | |
710 |
Tensile Strength: Ultimate (UTS), MPa | 580 to 620 | |
1190 |
Tensile Strength: Yield (Proof), MPa | 320 to 460 | |
800 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
320 |
Maximum Temperature: Mechanical, °C | 400 | |
1000 |
Melting Completion (Liquidus), °C | 1460 | |
1370 |
Melting Onset (Solidus), °C | 1420 | |
1320 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Expansion, µm/m-K | 12 | |
13 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.1 | |
75 |
Density, g/cm3 | 7.8 | |
8.3 |
Embodied Carbon, kg CO2/kg material | 1.5 | |
10 |
Embodied Energy, MJ/kg | 19 | |
140 |
Embodied Water, L/kg | 48 | |
360 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 110 to 120 | |
120 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 270 to 550 | |
1610 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
23 |
Strength to Weight: Axial, points | 21 to 22 | |
40 |
Strength to Weight: Bending, points | 20 to 21 | |
30 |
Thermal Shock Resistance, points | 18 to 19 | |
34 |
Alloy Composition
Aluminum (Al), % | 0 | |
2.5 to 3.3 |
Boron (B), % | 0 | |
0.0030 to 0.010 |
Carbon (C), % | 0.17 to 0.23 | |
0 to 0.15 |
Chromium (Cr), % | 0 to 0.4 | |
15 to 20 |
Cobalt (Co), % | 0 | |
13 to 20 |
Copper (Cu), % | 0 | |
0 to 0.15 |
Iron (Fe), % | 96.9 to 98.8 | |
0 to 4.0 |
Manganese (Mn), % | 1.0 to 1.5 | |
0 to 0.75 |
Molybdenum (Mo), % | 0 to 0.1 | |
3.0 to 5.0 |
Nickel (Ni), % | 0 to 0.4 | |
42.7 to 64 |
Phosphorus (P), % | 0 to 0.035 | |
0 to 0.015 |
Silicon (Si), % | 0 to 0.4 | |
0 to 0.75 |
Sulfur (S), % | 0 to 0.035 | |
0 to 0.015 |
Titanium (Ti), % | 0 | |
2.5 to 3.3 |