EN 1.1147 Steel vs. EN 1.4646 Stainless Steel
Both EN 1.1147 steel and EN 1.4646 stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.1147 steel and the bottom bar is EN 1.4646 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 110 to 140 | |
| 220 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 12 to 17 | |
| 34 |
| Fatigue Strength, MPa | 180 to 250 | |
| 340 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 280 | |
| 500 |
| Tensile Strength: Ultimate (UTS), MPa | 390 to 470 | |
| 750 |
| Tensile Strength: Yield (Proof), MPa | 280 to 370 | |
| 430 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 290 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 910 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1390 |
| Melting Onset (Solidus), °C | 1420 | |
| 1340 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Expansion, µm/m-K | 12 | |
| 17 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 13 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.8 |
| Embodied Energy, MJ/kg | 18 | |
| 41 |
| Embodied Water, L/kg | 46 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 40 to 73 | |
| 220 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 210 to 370 | |
| 460 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 14 to 17 | |
| 27 |
| Strength to Weight: Bending, points | 15 to 17 | |
| 24 |
| Thermal Shock Resistance, points | 12 to 15 | |
| 16 |
Alloy Composition
| Carbon (C), % | 0.15 to 0.19 | |
| 0.020 to 0.1 |
| Chromium (Cr), % | 0 | |
| 17 to 19 |
| Copper (Cu), % | 0 to 0.25 | |
| 1.5 to 3.0 |
| Iron (Fe), % | 98.3 to 99.25 | |
| 59 to 67.3 |
| Manganese (Mn), % | 0.6 to 0.9 | |
| 10.5 to 12.5 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.5 |
| Nickel (Ni), % | 0 | |
| 3.5 to 4.5 |
| Nitrogen (N), % | 0 | |
| 0.2 to 0.3 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 0.3 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |