EN 1.1152 Steel vs. S35135 Stainless Steel
Both EN 1.1152 steel and S35135 stainless steel are iron alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.1152 steel and the bottom bar is S35135 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 12 to 22 | |
| 34 |
| Fatigue Strength, MPa | 190 to 300 | |
| 180 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 79 |
| Shear Strength, MPa | 290 to 340 | |
| 390 |
| Tensile Strength: Ultimate (UTS), MPa | 400 to 550 | |
| 590 |
| Tensile Strength: Yield (Proof), MPa | 270 to 440 | |
| 230 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 1100 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1430 |
| Melting Onset (Solidus), °C | 1420 | |
| 1380 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Expansion, µm/m-K | 12 | |
| 16 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 37 |
| Density, g/cm3 | 7.8 | |
| 8.1 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 6.8 |
| Embodied Energy, MJ/kg | 18 | |
| 94 |
| Embodied Water, L/kg | 46 | |
| 220 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 41 to 110 | |
| 160 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 200 to 530 | |
| 130 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 14 to 19 | |
| 20 |
| Strength to Weight: Bending, points | 15 to 19 | |
| 19 |
| Thermal Shock Resistance, points | 13 to 17 | |
| 13 |
Alloy Composition
| Carbon (C), % | 0.18 to 0.22 | |
| 0 to 0.080 |
| Chromium (Cr), % | 0 | |
| 20 to 25 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 to 0.75 |
| Iron (Fe), % | 98.6 to 99.52 | |
| 28.3 to 45 |
| Manganese (Mn), % | 0.3 to 0.6 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0 | |
| 4.0 to 4.8 |
| Nickel (Ni), % | 0 | |
| 30 to 38 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 0.3 | |
| 0.6 to 1.0 |
| Sulfur (S), % | 0 to 0.025 | |
| 0 to 0.015 |
| Titanium (Ti), % | 0 | |
| 0.4 to 1.0 |