EN 1.1165 Cast Steel vs. EN 1.3961 Alloy
Both EN 1.1165 cast steel and EN 1.3961 alloy are iron alloys. They have 63% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.1165 cast steel and the bottom bar is EN 1.3961 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 11 to 20 | |
31 |
Poisson's Ratio | 0.29 | |
0.3 |
Shear Modulus, GPa | 73 | |
72 |
Tensile Strength: Ultimate (UTS), MPa | 600 to 780 | |
450 |
Tensile Strength: Yield (Proof), MPa | 290 to 620 | |
310 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
270 |
Melting Completion (Liquidus), °C | 1460 | |
1430 |
Melting Onset (Solidus), °C | 1420 | |
1390 |
Specific Heat Capacity, J/kg-K | 470 | |
460 |
Thermal Expansion, µm/m-K | 12 | |
1.3 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 1.9 | |
25 |
Density, g/cm3 | 7.8 | |
8.2 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
4.8 |
Embodied Energy, MJ/kg | 19 | |
66 |
Embodied Water, L/kg | 47 | |
110 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 to 100 | |
130 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 1010 | |
250 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
23 |
Strength to Weight: Axial, points | 21 to 28 | |
15 |
Strength to Weight: Bending, points | 20 to 24 | |
16 |
Thermal Shock Resistance, points | 19 to 25 | |
130 |
Alloy Composition
Carbon (C), % | 0.25 to 0.32 | |
0 to 0.050 |
Chromium (Cr), % | 0 | |
0 to 0.25 |
Iron (Fe), % | 97.2 to 98.6 | |
60.7 to 65 |
Manganese (Mn), % | 1.2 to 1.8 | |
0 to 0.5 |
Molybdenum (Mo), % | 0 | |
0 to 1.0 |
Nickel (Ni), % | 0 | |
35 to 37 |
Phosphorus (P), % | 0 to 0.035 | |
0 to 0.030 |
Silicon (Si), % | 0 to 0.6 | |
0 to 0.5 |
Sulfur (S), % | 0 to 0.030 | |
0 to 0.020 |