EN 1.1165 Cast Steel vs. N07041 Nickel
EN 1.1165 cast steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is EN 1.1165 cast steel and the bottom bar is N07041 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 220 |
| Elongation at Break, % | 11 to 20 | |
| 14 |
| Fatigue Strength, MPa | 200 to 380 | |
| 540 |
| Tensile Strength: Ultimate (UTS), MPa | 600 to 780 | |
| 1400 |
| Tensile Strength: Yield (Proof), MPa | 290 to 620 | |
| 1050 |
Thermal Properties
| Melting Onset (Solidus), °C | 1420 | |
| 1320 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Conductivity, W/m-K | 51 | |
| 11 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.2 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 81 to 100 | |
| 180 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 230 to 1010 | |
| 2510 |
| Stiffness to Weight: Axial, points | 13 | |
| 15 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 21 to 28 | |
| 47 |
| Strength to Weight: Bending, points | 20 to 24 | |
| 34 |
| Thermal Diffusivity, mm2/s | 14 | |
| 3.0 |
| Thermal Shock Resistance, points | 19 to 25 | |
| 38 |