EN 1.1170 Steel vs. EN 1.7362 Steel

Both EN 1.1170 steel and EN 1.7362 steel are iron alloys. They have a moderately high 95% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.1170 steel and the bottom bar is EN 1.7362 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180 to 210
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 16 to 17
21 to 22
Fatigue Strength, MPa 220 to 330
140 to 250
Impact Strength: V-Notched Charpy, J 28 to 35
38 to 46
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
74
Shear Strength, MPa 390 to 450
320 to 370
Tensile Strength: Ultimate (UTS), MPa 640 to 730
510 to 600
Tensile Strength: Yield (Proof), MPa 330 to 500
200 to 360

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Maximum Temperature: Mechanical, °C 400
510
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
40
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
8.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
9.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
4.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 19
23
Embodied Water, L/kg 49
69

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 91 to 100
90 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 290 to 670
100 to 340
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 23 to 26
18 to 21
Strength to Weight: Bending, points 21 to 23
18 to 20
Thermal Diffusivity, mm2/s 13
11
Thermal Shock Resistance, points 20 to 23
14 to 17

Alloy Composition

Carbon (C), % 0.25 to 0.32
0.1 to 0.15
Chromium (Cr), % 0 to 0.4
4.0 to 6.0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 96.7 to 98.5
91.5 to 95.2
Manganese (Mn), % 1.3 to 1.7
0.3 to 0.6
Molybdenum (Mo), % 0 to 0.1
0.45 to 0.65
Nickel (Ni), % 0 to 0.4
0 to 0.3
Nitrogen (N), % 0
0 to 0.012
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.035
0 to 0.0050

Comparable Variants