EN 1.1170 Steel vs. SAE-AISI 1137 Steel
Both EN 1.1170 steel and SAE-AISI 1137 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.
For each property being compared, the top bar is EN 1.1170 steel and the bottom bar is SAE-AISI 1137 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 210 | |
| 200 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 16 to 17 | |
| 11 to 17 |
| Fatigue Strength, MPa | 220 to 330 | |
| 250 to 400 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 73 | |
| 73 |
| Shear Strength, MPa | 390 to 450 | |
| 430 to 460 |
| Tensile Strength: Ultimate (UTS), MPa | 640 to 730 | |
| 700 to 760 |
| Tensile Strength: Yield (Proof), MPa | 330 to 500 | |
| 370 to 650 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 50 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 10 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.4 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 49 | |
| 48 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 91 to 100 | |
| 81 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 290 to 670 | |
| 360 to 1130 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 23 to 26 | |
| 25 to 27 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 22 to 24 |
| Thermal Diffusivity, mm2/s | 13 | |
| 14 |
| Thermal Shock Resistance, points | 20 to 23 | |
| 21 to 23 |
Alloy Composition
| Carbon (C), % | 0.25 to 0.32 | |
| 0.32 to 0.39 |
| Chromium (Cr), % | 0 to 0.4 | |
| 0 |
| Iron (Fe), % | 96.7 to 98.5 | |
| 97.8 to 98.3 |
| Manganese (Mn), % | 1.3 to 1.7 | |
| 1.4 to 1.7 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Nickel (Ni), % | 0 to 0.4 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.035 | |
| 0.080 to 0.13 |