EN 1.1172 Steel vs. Automotive Malleable Cast Iron
Both EN 1.1172 steel and automotive malleable cast iron are iron alloys. They have a very high 96% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.1172 steel and the bottom bar is automotive malleable cast iron.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 140 to 170 | |
| 130 to 290 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 180 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 70 |
| Tensile Strength: Ultimate (UTS), MPa | 480 to 1720 | |
| 350 to 720 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 260 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1410 |
| Melting Onset (Solidus), °C | 1420 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 51 | |
| 41 |
| Thermal Expansion, µm/m-K | 12 | |
| 14 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.1 | |
| 8.7 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.8 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.6 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 18 | |
| 20 |
| Embodied Water, L/kg | 46 | |
| 45 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 17 to 61 | |
| 13 to 26 |
| Strength to Weight: Bending, points | 17 to 41 | |
| 14 to 24 |
| Thermal Diffusivity, mm2/s | 14 | |
| 11 |
| Thermal Shock Resistance, points | 15 to 55 | |
| 9.9 to 21 |
Alloy Composition
| Carbon (C), % | 0.32 to 0.39 | |
| 2.2 to 2.9 |
| Copper (Cu), % | 0 to 0.25 | |
| 0 |
| Iron (Fe), % | 98.2 to 99.18 | |
| 93.6 to 96.7 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 0.15 to 1.3 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0.020 to 0.15 |
| Silicon (Si), % | 0 to 0.3 | |
| 0.9 to 1.9 |
| Sulfur (S), % | 0 to 0.025 | |
| 0.020 to 0.2 |