EN 1.1191 Steel vs. EN 1.1170 Steel
Both EN 1.1191 steel and EN 1.1170 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.1191 steel and the bottom bar is EN 1.1170 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 to 200 | |
| 180 to 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 16 to 17 | |
| 16 to 17 |
| Fatigue Strength, MPa | 210 to 290 | |
| 220 to 330 |
| Impact Strength: V-Notched Charpy, J | 16 to 29 | |
| 28 to 35 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Shear Strength, MPa | 380 to 430 | |
| 390 to 450 |
| Tensile Strength: Ultimate (UTS), MPa | 630 to 700 | |
| 640 to 730 |
| Tensile Strength: Yield (Proof), MPa | 310 to 440 | |
| 330 to 500 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1460 |
| Melting Onset (Solidus), °C | 1420 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 48 | |
| 50 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.1 | |
| 2.1 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.5 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 47 | |
| 49 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 83 to 100 | |
| 91 to 100 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 260 to 510 | |
| 290 to 670 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 25 | |
| 23 to 26 |
| Strength to Weight: Bending, points | 21 to 22 | |
| 21 to 23 |
| Thermal Diffusivity, mm2/s | 13 | |
| 13 |
| Thermal Shock Resistance, points | 20 to 22 | |
| 20 to 23 |
Alloy Composition
| Carbon (C), % | 0.42 to 0.5 | |
| 0.25 to 0.32 |
| Chromium (Cr), % | 0 to 0.4 | |
| 0 to 0.4 |
| Iron (Fe), % | 97.3 to 99.08 | |
| 96.7 to 98.5 |
| Manganese (Mn), % | 0.5 to 0.8 | |
| 1.3 to 1.7 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 to 0.1 |
| Nickel (Ni), % | 0 to 0.4 | |
| 0 to 0.4 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.035 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.035 | |
| 0 to 0.035 |