EN 1.1191 Steel vs. Monel R-405

EN 1.1191 steel belongs to the iron alloys classification, while Monel R-405 belongs to the nickel alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.1191 steel and the bottom bar is Monel R-405.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
160
Elongation at Break, % 16 to 17
9.1 to 39
Fatigue Strength, MPa 210 to 290
210 to 250
Poisson's Ratio 0.29
0.32
Shear Modulus, GPa 72
62
Shear Strength, MPa 380 to 430
350 to 370
Tensile Strength: Ultimate (UTS), MPa 630 to 700
540 to 630
Tensile Strength: Yield (Proof), MPa 310 to 440
190 to 350

Thermal Properties

Latent Heat of Fusion, J/g 250
270
Maximum Temperature: Mechanical, °C 400
900
Melting Completion (Liquidus), °C 1460
1350
Melting Onset (Solidus), °C 1420
1300
Specific Heat Capacity, J/kg-K 470
430
Thermal Conductivity, W/m-K 48
23
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
3.4
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
3.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
50
Density, g/cm3 7.8
8.9
Embodied Carbon, kg CO2/kg material 1.4
7.9
Embodied Energy, MJ/kg 19
110
Embodied Water, L/kg 47
250

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 83 to 100
49 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 260 to 510
120 to 370
Stiffness to Weight: Axial, points 13
10
Stiffness to Weight: Bending, points 24
21
Strength to Weight: Axial, points 22 to 25
17 to 20
Strength to Weight: Bending, points 21 to 22
17 to 18
Thermal Diffusivity, mm2/s 13
5.9
Thermal Shock Resistance, points 20 to 22
17 to 20

Alloy Composition

Carbon (C), % 0.42 to 0.5
0 to 0.3
Chromium (Cr), % 0 to 0.4
0
Copper (Cu), % 0
28 to 34
Iron (Fe), % 97.3 to 99.08
0 to 2.5
Manganese (Mn), % 0.5 to 0.8
0 to 2.0
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
63 to 72
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.035
0.025 to 0.060