EN 1.1203 Steel vs. AISI 446 Stainless Steel

Both EN 1.1203 steel and AISI 446 stainless steel are iron alloys. They have 75% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.1203 steel and the bottom bar is AISI 446 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 230
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 12 to 15
23
Fatigue Strength, MPa 210 to 310
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 72
79
Shear Strength, MPa 420 to 480
360
Tensile Strength: Ultimate (UTS), MPa 690 to 780
570
Tensile Strength: Yield (Proof), MPa 340 to 480
300

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
1180
Melting Completion (Liquidus), °C 1460
1510
Melting Onset (Solidus), °C 1420
1430
Specific Heat Capacity, J/kg-K 470
490
Thermal Conductivity, W/m-K 48
17
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
12
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.4
2.4
Embodied Energy, MJ/kg 19
35
Embodied Water, L/kg 47
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 69 to 100
110
Resilience: Unit (Modulus of Resilience), kJ/m3 310 to 610
230
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
26
Strength to Weight: Axial, points 25 to 28
21
Strength to Weight: Bending, points 22 to 24
20
Thermal Diffusivity, mm2/s 13
4.6
Thermal Shock Resistance, points 22 to 25
19

Alloy Composition

Carbon (C), % 0.52 to 0.6
0 to 0.2
Chromium (Cr), % 0 to 0.4
23 to 27
Iron (Fe), % 97.1 to 98.9
69.2 to 77
Manganese (Mn), % 0.6 to 0.9
0 to 1.5
Molybdenum (Mo), % 0 to 0.1
0
Nickel (Ni), % 0 to 0.4
0 to 0.75
Nitrogen (N), % 0
0 to 0.25
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.030