MakeItFrom.com
Menu (ESC)

EN 1.1203 Steel vs. EN 1.7231 Steel

Both EN 1.1203 steel and EN 1.7231 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.1203 steel and the bottom bar is EN 1.7231 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 230
240 to 280
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 12 to 15
11 to 12
Fatigue Strength, MPa 210 to 310
360 to 500
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 690 to 780
790 to 930
Tensile Strength: Yield (Proof), MPa 340 to 480
570 to 800

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 48
46
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.5
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 47
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 69 to 100
87 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 310 to 610
870 to 1700
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 28
28 to 33
Strength to Weight: Bending, points 22 to 24
24 to 27
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 22 to 25
23 to 27

Alloy Composition

Carbon (C), % 0.52 to 0.6
0.38 to 0.45
Chromium (Cr), % 0 to 0.4
0.8 to 1.2
Iron (Fe), % 97.1 to 98.9
96.4 to 98.1
Manganese (Mn), % 0.6 to 0.9
0.6 to 1.0
Molybdenum (Mo), % 0 to 0.1
0.15 to 0.3
Nickel (Ni), % 0 to 0.4
0
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 0.4
0 to 0.6
Sulfur (S), % 0 to 0.035
0 to 0.030