EN 1.1203 Steel vs. SAE-AISI 5160 Steel
Both EN 1.1203 steel and SAE-AISI 5160 steel are iron alloys. Their average alloy composition is basically identical.
For each property being compared, the top bar is EN 1.1203 steel and the bottom bar is SAE-AISI 5160 steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 200 to 230 | |
200 to 340 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
190 |
Elongation at Break, % | 12 to 15 | |
12 to 18 |
Fatigue Strength, MPa | 210 to 310 | |
180 to 650 |
Poisson's Ratio | 0.29 | |
0.29 |
Shear Modulus, GPa | 72 | |
73 |
Shear Strength, MPa | 420 to 480 | |
390 to 700 |
Tensile Strength: Ultimate (UTS), MPa | 690 to 780 | |
660 to 1150 |
Tensile Strength: Yield (Proof), MPa | 340 to 480 | |
280 to 1010 |
Thermal Properties
Latent Heat of Fusion, J/g | 250 | |
250 |
Maximum Temperature: Mechanical, °C | 400 | |
420 |
Melting Completion (Liquidus), °C | 1460 | |
1450 |
Melting Onset (Solidus), °C | 1420 | |
1410 |
Specific Heat Capacity, J/kg-K | 470 | |
470 |
Thermal Conductivity, W/m-K | 48 | |
43 |
Thermal Expansion, µm/m-K | 12 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 7.2 | |
7.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 8.3 | |
8.3 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 2.1 | |
2.1 |
Density, g/cm3 | 7.8 | |
7.8 |
Embodied Carbon, kg CO2/kg material | 1.4 | |
1.4 |
Embodied Energy, MJ/kg | 19 | |
19 |
Embodied Water, L/kg | 47 | |
50 |
Common Calculations
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 69 to 100 | |
73 to 160 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 310 to 610 | |
200 to 2700 |
Stiffness to Weight: Axial, points | 13 | |
13 |
Stiffness to Weight: Bending, points | 24 | |
24 |
Strength to Weight: Axial, points | 25 to 28 | |
23 to 41 |
Strength to Weight: Bending, points | 22 to 24 | |
22 to 31 |
Thermal Diffusivity, mm2/s | 13 | |
12 |
Thermal Shock Resistance, points | 22 to 25 | |
19 to 34 |
Alloy Composition
Carbon (C), % | 0.52 to 0.6 | |
0.56 to 0.61 |
Chromium (Cr), % | 0 to 0.4 | |
0.7 to 0.9 |
Iron (Fe), % | 97.1 to 98.9 | |
97.1 to 97.8 |
Manganese (Mn), % | 0.6 to 0.9 | |
0.75 to 1.0 |
Molybdenum (Mo), % | 0 to 0.1 | |
0 |
Nickel (Ni), % | 0 to 0.4 | |
0 |
Phosphorus (P), % | 0 to 0.035 | |
0 to 0.035 |
Silicon (Si), % | 0 to 0.4 | |
0.15 to 0.35 |
Sulfur (S), % | 0 to 0.035 | |
0 to 0.040 |