EN 1.1219 Steel vs. SAE-AISI 4012 Steel

Both EN 1.1219 steel and SAE-AISI 4012 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.1219 steel and the bottom bar is SAE-AISI 4012 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 220
130
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
73
Tensile Strength: Ultimate (UTS), MPa 700 to 770
420

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
51
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
47

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
15
Strength to Weight: Bending, points 22 to 24
16
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 22 to 25
12

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.52 to 0.6
0.090 to 0.14
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 98.3 to 99.4
98.2 to 98.9
Manganese (Mn), % 0.6 to 0.9
0.75 to 1.0
Molybdenum (Mo), % 0
0.15 to 0.25
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0 to 0.4
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.040