EN 1.1219 Steel vs. SAE-AISI 52100 Steel

Both EN 1.1219 steel and SAE-AISI 52100 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.1219 steel and the bottom bar is SAE-AISI 52100 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 200 to 220
180 to 210
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 72
72
Tensile Strength: Ultimate (UTS), MPa 700 to 770
590 to 2010

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
430
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
47
Thermal Expansion, µm/m-K 12
12 to 13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.1
8.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.9
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 47
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 25 to 27
21 to 72
Strength to Weight: Bending, points 22 to 24
20 to 45
Thermal Diffusivity, mm2/s 14
13
Thermal Shock Resistance, points 22 to 25
19 to 61

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.52 to 0.6
0.93 to 1.1
Chromium (Cr), % 0
1.4 to 1.6
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 98.3 to 99.4
96.5 to 97.3
Manganese (Mn), % 0.6 to 0.9
0.25 to 0.45
Oxygen (O), % 0 to 0.0020
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.4
0.15 to 0.35
Sulfur (S), % 0 to 0.030
0 to 0.015

Comparable Variants