EN 1.1233 Steel vs. EN 1.5510 Steel
Both EN 1.1233 steel and EN 1.5510 steel are iron alloys. Their average alloy composition is basically identical. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.1233 steel and the bottom bar is EN 1.5510 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 220 | |
| 130 to 190 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 760 | |
| 450 to 1600 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 51 | |
| 51 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 1.4 |
| Embodied Energy, MJ/kg | 19 | |
| 19 |
| Embodied Water, L/kg | 47 | |
| 47 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 24 to 27 | |
| 16 to 57 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 17 to 39 |
| Thermal Diffusivity, mm2/s | 14 | |
| 14 |
| Thermal Shock Resistance, points | 22 to 24 | |
| 13 to 47 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 |
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0.52 to 0.6 | |
| 0.25 to 0.3 |
| Chromium (Cr), % | 0 | |
| 0 to 0.3 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.25 |
| Iron (Fe), % | 98 to 99.1 | |
| 97.9 to 99.149 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0.6 to 0.9 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |