EN 1.1233 Steel vs. CC750S Brass
EN 1.1233 steel belongs to the iron alloys classification, while CC750S brass belongs to the copper alloys. There are 25 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.1233 steel and the bottom bar is CC750S brass.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 200 to 220 | |
| 54 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Poisson's Ratio | 0.29 | |
| 0.31 |
| Shear Modulus, GPa | 72 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 760 | |
| 200 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 170 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 130 |
| Melting Completion (Liquidus), °C | 1450 | |
| 860 |
| Melting Onset (Solidus), °C | 1410 | |
| 810 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 380 |
| Thermal Conductivity, W/m-K | 51 | |
| 110 |
| Thermal Expansion, µm/m-K | 12 | |
| 20 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 24 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 25 |
| Density, g/cm3 | 7.8 | |
| 8.2 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.8 |
| Embodied Energy, MJ/kg | 19 | |
| 46 |
| Embodied Water, L/kg | 47 | |
| 330 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.1 |
| Stiffness to Weight: Bending, points | 24 | |
| 19 |
| Strength to Weight: Axial, points | 24 to 27 | |
| 6.8 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 9.3 |
| Thermal Diffusivity, mm2/s | 14 | |
| 35 |
| Thermal Shock Resistance, points | 22 to 24 | |
| 6.7 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 to 0.1 |
| Carbon (C), % | 0.52 to 0.6 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 62 to 67 |
| Iron (Fe), % | 98 to 99.1 | |
| 0 to 0.8 |
| Lead (Pb), % | 0 | |
| 1.0 to 3.0 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0 to 0.2 |
| Nickel (Ni), % | 0 | |
| 0 to 1.0 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.050 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.050 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 1.5 |
| Zinc (Zn), % | 0 | |
| 26.3 to 36 |