EN 1.1233 Steel vs. N06060 Nickel
EN 1.1233 steel belongs to the iron alloys classification, while N06060 nickel belongs to the nickel alloys. There are 20 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is EN 1.1233 steel and the bottom bar is N06060 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 210 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 82 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 760 | |
| 700 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 980 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1510 |
| Melting Onset (Solidus), °C | 1410 | |
| 1450 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 430 |
| Thermal Expansion, µm/m-K | 12 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 65 |
| Density, g/cm3 | 7.8 | |
| 8.7 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 12 |
| Embodied Energy, MJ/kg | 19 | |
| 160 |
| Embodied Water, L/kg | 47 | |
| 280 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 24 to 27 | |
| 22 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 20 |
| Thermal Shock Resistance, points | 22 to 24 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0.52 to 0.6 | |
| 0 to 0.030 |
| Chromium (Cr), % | 0 | |
| 19 to 22 |
| Copper (Cu), % | 0 to 0.3 | |
| 0.25 to 1.3 |
| Iron (Fe), % | 98 to 99.1 | |
| 0 to 14 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0 to 1.5 |
| Molybdenum (Mo), % | 0 | |
| 12 to 14 |
| Nickel (Ni), % | 0 | |
| 54 to 60 |
| Niobium (Nb), % | 0 | |
| 0.5 to 1.3 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 to 0.5 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.0050 |
| Tungsten (W), % | 0 | |
| 0.25 to 1.3 |