EN 1.1233 Steel vs. Z41121 Zinc
EN 1.1233 steel belongs to the iron alloys classification, while Z41121 zinc belongs to the zinc alloys. There are 24 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.
For each property being compared, the top bar is EN 1.1233 steel and the bottom bar is Z41121 zinc.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 87 |
| Poisson's Ratio | 0.29 | |
| 0.25 |
| Shear Modulus, GPa | 72 | |
| 35 |
| Tensile Strength: Ultimate (UTS), MPa | 680 to 760 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 110 |
| Maximum Temperature: Mechanical, °C | 400 | |
| 90 |
| Melting Completion (Liquidus), °C | 1450 | |
| 410 |
| Melting Onset (Solidus), °C | 1410 | |
| 400 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 390 |
| Thermal Conductivity, W/m-K | 51 | |
| 110 |
| Thermal Expansion, µm/m-K | 12 | |
| 26 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.1 | |
| 27 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.2 | |
| 37 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 1.9 | |
| 11 |
| Density, g/cm3 | 7.8 | |
| 6.6 |
| Embodied Carbon, kg CO2/kg material | 1.4 | |
| 2.8 |
| Embodied Energy, MJ/kg | 19 | |
| 54 |
| Embodied Water, L/kg | 47 | |
| 340 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 7.4 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 24 to 27 | |
| 6.1 |
| Strength to Weight: Bending, points | 22 to 24 | |
| 9.3 |
| Thermal Diffusivity, mm2/s | 14 | |
| 44 |
| Thermal Shock Resistance, points | 22 to 24 | |
| 4.6 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 to 0.010 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0050 |
| Carbon (C), % | 0.52 to 0.6 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0.080 to 0.49 |
| Iron (Fe), % | 98 to 99.1 | |
| 0 to 0.010 |
| Lead (Pb), % | 0 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0.9 to 1.2 | |
| 0 |
| Oxygen (O), % | 0 to 0.0020 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0 to 0.4 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.0030 |
| Titanium (Ti), % | 0 | |
| 0.050 to 0.18 |
| Zinc (Zn), % | 0 | |
| 99.292 to 99.87 |