EN 1.3518 Steel vs. EN 1.3967 Stainless Steel

Both EN 1.3518 steel and EN 1.3967 stainless steel are iron alloys. They have 57% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.3518 steel and the bottom bar is EN 1.3967 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
79
Tensile Strength: Ultimate (UTS), MPa 630
690

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 420
1070
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1380
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 13
16

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
25
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
4.8
Embodied Energy, MJ/kg 20
66
Embodied Water, L/kg 51
180

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
24
Strength to Weight: Bending, points 21
22
Thermal Shock Resistance, points 19
15

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.93 to 1.1
0 to 0.030
Chromium (Cr), % 0.9 to 1.2
20 to 21.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.3 to 97.8
50.3 to 57.8
Manganese (Mn), % 0.9 to 1.2
4.0 to 6.0
Molybdenum (Mo), % 0 to 0.1
3.0 to 3.5
Nickel (Ni), % 0
15 to 17
Niobium (Nb), % 0
0 to 0.25
Nitrogen (N), % 0
0.2 to 0.35
Oxygen (O), % 0 to 0.0015
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0.45 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.010