EN 1.3518 Steel vs. S32550 Stainless Steel

Both EN 1.3518 steel and S32550 stainless steel are iron alloys. They have 65% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.3518 steel and the bottom bar is S32550 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
260
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 72
80
Tensile Strength: Ultimate (UTS), MPa 630
860

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Maximum Temperature: Mechanical, °C 420
1100
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 43
16
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.4
20
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.5
3.8
Embodied Energy, MJ/kg 20
53
Embodied Water, L/kg 51
180

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 23
31
Strength to Weight: Bending, points 21
26
Thermal Diffusivity, mm2/s 12
4.4
Thermal Shock Resistance, points 19
23

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.93 to 1.1
0 to 0.040
Chromium (Cr), % 0.9 to 1.2
24 to 27
Copper (Cu), % 0 to 0.3
1.5 to 2.5
Iron (Fe), % 96.3 to 97.8
57.2 to 67
Manganese (Mn), % 0.9 to 1.2
0 to 1.5
Molybdenum (Mo), % 0 to 0.1
2.9 to 3.9
Nickel (Ni), % 0
4.5 to 6.5
Nitrogen (N), % 0
0.1 to 0.25
Oxygen (O), % 0 to 0.0015
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.45 to 0.75
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030