EN 1.3519 Steel vs. EN 1.4424 Stainless Steel

Both EN 1.3519 steel and EN 1.4424 stainless steel are iron alloys. They have 74% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.3519 steel and the bottom bar is EN 1.4424 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190 to 220
230
Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
78
Tensile Strength: Ultimate (UTS), MPa 620 to 730
800

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Maximum Temperature: Mechanical, °C 430
960
Melting Completion (Liquidus), °C 1440
1430
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 43
13
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.5
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.7
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 2.6
15
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.5
3.4
Embodied Energy, MJ/kg 21
46
Embodied Water, L/kg 55
140

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22 to 26
29
Strength to Weight: Bending, points 21 to 23
25
Thermal Diffusivity, mm2/s 12
3.5
Thermal Shock Resistance, points 18 to 22
23

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Carbon (C), % 0.93 to 1.1
0 to 0.030
Chromium (Cr), % 1.4 to 1.7
18 to 19
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 95.4 to 96.8
68.6 to 72.4
Manganese (Mn), % 1.4 to 1.7
1.2 to 2.0
Molybdenum (Mo), % 0 to 0.1
2.5 to 3.0
Nickel (Ni), % 0
4.5 to 5.2
Nitrogen (N), % 0
0.050 to 0.1
Oxygen (O), % 0 to 0.0015
0
Phosphorus (P), % 0 to 0.025
0 to 0.035
Silicon (Si), % 0.45 to 0.75
1.4 to 2.0
Sulfur (S), % 0 to 0.030
0 to 0.015