EN 1.3519 Steel vs. EN 1.6771 Steel
Both EN 1.3519 steel and EN 1.6771 steel are iron alloys. They have a very high 96% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is EN 1.3519 steel and the bottom bar is EN 1.6771 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 220 | |
| 280 to 350 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 730 | |
| 930 to 1180 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 440 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 43 | |
| 46 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.5 | |
| 8.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.7 | |
| 9.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 5.0 |
| Density, g/cm3 | 7.8 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.9 |
| Embodied Energy, MJ/kg | 21 | |
| 25 |
| Embodied Water, L/kg | 55 | |
| 58 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 22 to 26 | |
| 33 to 41 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 27 to 31 |
| Thermal Diffusivity, mm2/s | 12 | |
| 13 |
| Thermal Shock Resistance, points | 18 to 22 | |
| 27 to 35 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0.93 to 1.1 | |
| 0.27 to 0.33 |
| Chromium (Cr), % | 1.4 to 1.7 | |
| 0.8 to 1.2 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 95.4 to 96.8 | |
| 92.2 to 95 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0.6 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0.3 to 0.6 |
| Nickel (Ni), % | 0 | |
| 3.0 to 4.0 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.45 to 0.75 | |
| 0 to 0.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.020 |