EN 1.3519 Steel vs. Grade 7 Babbitt Metal
EN 1.3519 steel belongs to the iron alloys classification, while grade 7 Babbitt Metal belongs to the otherwise unclassified metals. There are 16 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.
For each property being compared, the top bar is EN 1.3519 steel and the bottom bar is grade 7 Babbitt Metal.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 220 | |
| 23 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 26 |
| Poisson's Ratio | 0.29 | |
| 0.4 |
| Shear Modulus, GPa | 72 | |
| 9.1 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 48 |
| Melting Completion (Liquidus), °C | 1440 | |
| 270 |
| Melting Onset (Solidus), °C | 1400 | |
| 240 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 150 |
| Thermal Expansion, µm/m-K | 13 | |
| 26 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 23 |
| Density, g/cm3 | 7.8 | |
| 10 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 4.4 |
| Embodied Energy, MJ/kg | 21 | |
| 62 |
| Embodied Water, L/kg | 55 | |
| 880 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 1.4 |
| Stiffness to Weight: Bending, points | 25 | |
| 9.6 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 to 0.0050 |
| Antimony (Sb), % | 0 | |
| 14 to 16 |
| Arsenic (As), % | 0 | |
| 0.3 to 0.6 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.050 |
| Carbon (C), % | 0.93 to 1.1 | |
| 0 |
| Chromium (Cr), % | 1.4 to 1.7 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 to 0.5 |
| Iron (Fe), % | 95.4 to 96.8 | |
| 0 to 0.1 |
| Lead (Pb), % | 0 | |
| 71.9 to 76.4 |
| Manganese (Mn), % | 1.4 to 1.7 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 |
| Silicon (Si), % | 0.45 to 0.75 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 9.3 to 10.7 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0050 |