EN 1.3520 Steel vs. EN 1.5024 Steel
Both EN 1.3520 steel and EN 1.5024 steel are iron alloys. They have a very high 98% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.3520 steel and the bottom bar is EN 1.5024 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 220 | |
| 200 to 470 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 620 to 730 | |
| 670 to 1930 |
Thermal Properties
| Latent Heat of Fusion, J/g | 260 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 430 | |
| 400 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1440 |
| Melting Onset (Solidus), °C | 1400 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 43 | |
| 50 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.6 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.6 | |
| 1.9 |
| Density, g/cm3 | 7.8 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.4 |
| Embodied Energy, MJ/kg | 20 | |
| 19 |
| Embodied Water, L/kg | 54 | |
| 45 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 22 to 26 | |
| 24 to 69 |
| Strength to Weight: Bending, points | 21 to 23 | |
| 22 to 45 |
| Thermal Diffusivity, mm2/s | 12 | |
| 14 |
| Thermal Shock Resistance, points | 18 to 22 | |
| 20 to 58 |
Alloy Composition
| Aluminum (Al), % | 0 to 0.050 | |
| 0 |
| Carbon (C), % | 0.93 to 1.1 | |
| 0.42 to 0.5 |
| Chromium (Cr), % | 1.4 to 1.7 | |
| 0 |
| Copper (Cu), % | 0 to 0.3 | |
| 0 |
| Iron (Fe), % | 95.9 to 97.2 | |
| 96.7 to 97.6 |
| Manganese (Mn), % | 1.0 to 1.2 | |
| 0.5 to 0.8 |
| Molybdenum (Mo), % | 0 to 0.1 | |
| 0 |
| Oxygen (O), % | 0 to 0.0015 | |
| 0 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.025 |
| Silicon (Si), % | 0.45 to 0.75 | |
| 1.5 to 2.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |